Browsing by Subject "Titanium"
Now showing 1 - 2 of 2
- Results Per Page
- Sort Options
Item Open Access Effect of surface topography on in vitro osteoblast function and mechanical performance of 3D printed titanium.(Journal of biomedical materials research. Part A, 2021-10) Abar, Bijan; Kelly, Cambre; Pham, Anh; Allen, Nicholas; Barber, Helena; Kelly, Alexander; Mirando, Anthony J; Hilton, Matthew J; Gall, Ken; Adams, Samuel BCritical-sized defects remain a significant challenge in orthopaedics. 3D printed scaffolds are a promising treatment but are still limited due to inconsistent osseous integration. The goal of the study is to understand how changing the surface roughness of 3D printed titanium either by surface treatment or artificially printing rough topography impacts the mechanical and biological properties of 3D printed titanium. Titanium tensile samples and discs were printed via laser powder bed fusion. Roughness was manipulated by post-processing printed samples or by directly printing rough features. Experimental groups in order of increasing surface roughness were Polished, Blasted, As Built, Sprouts, and Rough Sprouts. Tensile behavior of samples showed reduced strength with increasing surface roughness. MC3T3 pre-osteoblasts were seeded on discs and analyzed for cellular proliferation, differentiation, and matrix deposition at 0, 2, and 4 weeks. Printing roughness diminished mechanical properties such as tensile strength and ductility without clear benefit to cell growth. Roughness features were printed on mesoscale, unlike samples in literature in which roughness on microscale demonstrated an increase in cell activity. The data suggest that printing artificial roughness on titanium scaffold is not an effective strategy to promote osseous integration.Item Open Access Evaluation of monoenergetic imaging to reduce metallic instrumentation artifacts in computed tomography of the cervical spine.(Journal of neurosurgery. Spine, 2015-01) Komlosi, Peter; Grady, Deborah; Smith, Justin S; Shaffrey, Christopher I; Goode, Allen R; Judy, Patricia G; Shaffrey, Mark; Wintermark, MaxObject
Monoenergetic imaging with dual-energy CT has been proposed to reduce metallic artifacts in comparison with conventional polychromatic CT. The purpose of this study is to systematically evaluate and define the optimal dual-energy CT imaging parameters for specific cervical spinal implant alloy compositions.Methods
Spinal fixation rods of cobalt-chromium or titanium alloy inserted into the cervical spine section of an Alderson Rando anthropomorphic phantom were imaged ex vivo with fast-kilovoltage switching CT at 80 and 140 peak kV. The collimation width and field of view were varied between 20 and 40 mm and medium to large, respectively. Extrapolated monoenergetic images were generated at 70, 90, 110, and 130 kiloelectron volts (keV). The standard deviation of voxel intensities along a circular line profile around the spine was used as an index of the magnitude of metallic artifact.Results
The metallic artifact was more conspicuous around the fixation rods made of cobalt-chromium than those of titanium alloy. The magnitude of metallic artifact seen with titanium fixation rods was minimized at monoenergies of 90 keV and higher, using a collimation width of 20 mm and large field of view. The magnitude of metallic artifact with cobalt-chromium fixation rods was minimized at monoenergies of 110 keV and higher; collimation width or field of view had no effect.Conclusions
Optimization of acquisition settings used with monoenergetic CT studies might yield reduced metallic artifacts.